VCN150 DIN 1.6582 Alloy Steel Plate 34CrNiMo6 En10083-3 Quenched And Tempered UT Operations
1.EN Steel 34CrNiMo6 Supply Range
Round Steel Bar Sizes: diameter 10mm – 3000mm
Steel Flat and Plate: 10mm-1500mm thickness x 200-3000mm width
Other steel shape and sizes available according to your requirements.
Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.
2.EN 34CrNiMo6 Steel Standards And Equivalents
| BS EN 10083 -3: 2006 | 34CrNiMo6 / 1.6582 | ASTM A29: 2004 | 4337 |
| BS EN 10250 – 3: 2000 |
3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties
| BS EN 10083 – 3:2006 | 34CrNiMo6
/1.6582 | C | Mn | Si | P | S | Cr | Mo | Ni |
| 0.30-0.38 | 0.5-0.8 | 0.40 max | 0.025 max | 0.035 max | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 |
| BS EN 10250-3:2000 | C | Mn | Si | P | S | Cr | Mo | Ni |
| 0.30-0.38 | 0.5-0.8 | 0.40 max | 0.035 max | 0.035 max | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 |
| ASTM A29: 2004 | 4337 | C | Mn | Si | P | S | Cr | Mo | Ni |
| 0.30-0.40 | 0.6-0.8 | 0.20-0.35 | 0.035 max | 0.040 max | 0.70-0.90 | 0.20-0.30 | 1.65-2.00 |
4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel
| Properties | < 16 | >16 – 40 | >40 – 100 | >100 – 160 | >160 – 250 |
| Thickness t [mm] | < 8 | 8<t<20 | 20<t<60 | 60<t<100 | 100<t<160 |
| Yield strength Re [N/mm²] | min. 1000 | min. 900 | min. 800 | min. 700 | min. 600 |
| Tensile strength Rm [N/mm2] | 1200 – 1400 | 1100 – 1300 | 1000 – 1200 | 900 – 1100 | 800 – 950 |
| Elongation A [%] | min. 9 | min. 10 | min. 11 | min. 12 | min. 13 |
| Reduction of area Z [%] | min. 40 | min. 45 | min. 50 | min. 55 | min. 55 |
| Toughness CVN [J] | min. 35 | min. 45 | min. 45 | min. 45 | min. 45 |
5.Heat Treatment of 34CrNiMo6 Engineering Steel
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel
- Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;
- Soak at this hardening temperature quench in oil;
- Temper as soon as 34CrNiMo6 steels reach room temperature.
- Heat uniformly to the suitable temperature;
- Withdraw from the furnace and cool in the air.
- The usual tempering temperature is 600°C which depending on the actual requirements.
6.Forging of DIN 34CrNiMo6 / 1.6582 Steel
Hot forming temperature: 1100-900oC.
7.Machinability of Steel 34CrNiMo6
Machining is best done with this 1.6582 alloy steel in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
8.Welding
The alloy materials can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.
9.Application
EN DIN 34CrNiMo6 steel is used to make tools which demands good plasticity and high strength. It is usually selected to make the big size and important parts, such as heavy machinery axle,turbine shaft blade, high load of transmission parts, fasteners, crank shafts, gears, as well as heavily loaded parts for motor construction etc.
Otai Steel is reliable to supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels. Please tell us your detailed requirements and have the best offer soon.